Fire Bricks

 

STANDART SIZE FIRE BRICK

 

 SK / TN - 30

No

Specification

SK/TN - 30

1.

Max.Service Temparature

(Temperature Kerja Maximum) 

  ( 0C )

1100

2.

Apparent Porosity

(Porositas)                            

  ( % )

21 - 25

3.

Bulk Density

(Berat Jenis)                        

   (gr / cm3 )

1,90 - 1,95

4.

Cold Crushing Strenght            

( kg / cm3 )

> 200

5.

Permanent Linear Change      

   ( % )

at 10500C

+ 0,42

6.

Chemical Composition

(Komposisi Kimia)

AI2O3

SiO2

> 26

< 70

 

 

 SK / TN - 32

No

Specification SK/TN - 32
1

Max.Service Temparature

(Temperature Kerja Maximum) 

  ( 0C )

1200
2

Apparent Porosity

(Porositas)                            

  ( % )

21 - 24
3

Bulk Density

(Berat Jenis)                        

   (gr / cm3 )

1,90 - 2,00
4

Cold Crushing Strenght            

( kg / cm3 )

> 225
5

Permanent Linear Change      

   ( % )

at 11500C

+ 0,40

6

Chemical Composition

(Komposisi Kimia)

AI2O3

SiO2

> 32

< 65

 

 

 SK / TN - 33

No Specification SK/TN - 33
1

Max.Service Temparature

(Temperature Kerja Maximum) 

  ( 0C )

1250
2

Apparent Porosity

(Porositas)                            

  ( % )

20 - 23
3

Bulk Density

(Berat Jenis)                        

   (gr / cm3 )

1,92 - 2,05
4

Cold Crushing Strenght            

( kg / cm3 )

> 250
5

Permanent Linear Change      

   ( % )

at 12000C

+ 0,35

6

Chemical Composition

(Komposisi Kimia)

AI2O3

SiO2

> 35

< 60

 

 

 SK / TN - 34

No Specification SK/TN - 34
1

Max.Service Temparature

(Temperature Kerja Maximum) 

  ( 0C )

1350
2

Apparent Porosity

(Porositas)                            

  ( % )

19 - 22
3

Bulk Density

(Berat Jenis)                        

   (gr / cm3 )

1,98 - 2,10
4

Cold Crushing Strenght            

( kg / cm3 )

> 300
5

Permanent Linear Change      

   ( % )

at 13000C

+ 0,32

6

Chemical Composition

(Komposisi Kimia)

AI2O3

SiO2

> 40

< 55

 

 

 SK / TN - 36

No Specification SK/TN - 36
1

Max.Service Temparature

(Temperature Kerja Maximum) 

  ( 0C )

1500
2

Apparent Porosity

(Porositas)                            

  ( % )

17 - 21
3

Bulk Density

(Berat Jenis)                        

   (gr / cm3 )

2,15 - 2,25
4

Cold Crushing Strenght            

( kg / cm3 )

>350
5

Permanent Linear Change      

   ( % )

at 14000C

+ 0,30

6

Chemical Composition

(Komposisi Kimia)

AI2O3

SiO2

> 50

< 45

 